Why is it that my plates turned a yellowy color? If you want to check, you can look at my project folder. But wherever there was soemthing touch (a bolt or washer, etc) it was normal SS color. Where there was electrolye, it turned color. Now, it is only SS304, but I was only using Lye. This shouldn't do it, as far as I know. Would amperage or lye concentrations have any affect at all?
Any ideas, I would love to know. It seemed to work fine still, but I am just curious. I don't know however, it may have affected efficiency? We'll see with further testing.